Zn vacancy formation, Zn evaporation and decomposition of ZnSb at elevated temperatures: Influence on the microstructure and the electrical properties

Publication date: 5 July 2017
Source:Journal of Alloys and Compounds, Volume 710
Author(s): Xin Song, Matthias Schrade, Nahum Masó, Terje G. Finstad
The influence of annealing on the microstructure and electrical properties of undoped polycrystalline ZnSb samples has been investigated by different experimental techniques. In situ XRD in an argon atmosphere showed that ZnSb powders decompose at 300 °C, which is attributed to Zn evaporation. In situ SEM in a moist atmosphere showed fast surface deterioration at 450 °C and above, reflecting decomposition of ZnSb and the formation of metallic Sb precipitates. The rate of Zn loss in a reducing atmosphere was determined by thermogravimetry and related to the Zn partial vapor pressure. The increase of the hole carrier concentration of ZnSb measured at room temperature after heat treatment was correlated with Zn evaporation at elevated temperature. The carrier concentration after annealing at 400 °C is consistent with an activation energy for Zn vacancy formation of 0.4 eV and a maximum Zn deficiency x of Zn1-xSb of 1 × 10−3.



http://ift.tt/2nK6VRe

Δεν υπάρχουν σχόλια:

Δημοσίευση σχολίου